Bola de molienda de material fundido de alta calidad
Composición química y dureza de la bola de fundición ZW:
1. Composición química
Name
|
Material
|
Chemical elements
|
Hardness
|
C
|
Si
|
Mn
|
S
|
P
|
Cr
|
HRC
|
Cast iron ball
|
Special cr1
|
2.0-3.0
|
<1.0
|
0.5-2.0
|
≤0.06
|
≤0.06
|
>20
|
60-65
|
Special cr2
|
2.0-3.0
|
<1.0
|
0.5-2.0
|
≤0.06
|
≤0.06
|
>15
|
58-64
|
High Cr
|
2.0-3.2
|
<1.0
|
0.5-2.5
|
≤0.06
|
≤0.06
|
>10
|
58-63
|
Medium Cr
|
2.0-3.2
|
<1.0
|
0.5-2.5
|
≤0.06
|
≤0.06
|
≥5
|
48-55
|
Low Cr
|
2.2-3.4
|
≤1.2
|
0.5-1.5
|
≤0.06
|
≤0.06
|
1.0-1.5
|
45-50
|
2. dureza
Material
|
20mm-40mm
HRC
|
50mm-80mm
HRC
|
90mm and above
HRC
|
Surface
|
Core
|
Surface
|
Core
|
Surface
|
Core
|
Special Cr:>20
|
60-65
|
60-65
|
60-65
|
60-65
|
60-65
|
58-63
|
Special Cr:>15
|
58-64
|
58-64
|
58-64
|
58-64
|
58-64
|
56-62
|
High Cr:>10
|
58-63
|
58-63
|
58-63
|
58-63
|
58-63
|
56-61
|
Medium Cr:≥5
|
48-55
|
48-55
|
48-55
|
48-55
|
48-55
|
46-53
|
Low Cr:1-1.5
|
45-50
|
45-50
|
45-50
|
45-50
|
45-50
|
43-48
|
Tipos de bolas de fundición ZW:
De acuerdo con los diferentes elementos químicos, las bolas de fundición se pueden dividir en Cr bajo, Cr medio y Cr alto. En la actualidad, los materiales anteriores son ampliamente utilizados en todo el mundo, es decir, los materiales convencionales, si hay necesidades especiales, se pueden personalizar.
Proceso de producción de bolas fundidas:
Las bolas de fundición se derriten en un horno eléctrico y se vierten en moldes después de proporciones científicas. Las bolas con alto contenido de cromo también se procesan mediante enfriamiento rápido con aceite.
Peso de bolas de hierro fundido
(mm)
Nominal diameter
|
(mm)
Diametrical Tolerance
|
(kg)
Approx weight per ball
|
Average number
per MT
|
20
|
+1,—0.5
|
0.033
|
30303
|
25
|
+1,—0.5
|
0.064
|
15635
|
30
|
+2.0,—1.0
|
0.11
|
9090
|
40
|
+2.0,—1.0
|
0.261
|
3831
|
50
|
+2.0,—1.0
|
0.510
|
1961
|
60
|
+2.0,—1.0
|
0.883
|
1132
|
70
|
+3.0,—1.5
|
1.402
|
713
|
80
|
+3.0,—1.5
|
2.092
|
478
|
90
|
+3.0,—1.5
|
2.98
|
335
|
100
|
+3.0,—1.5
|
4.087
|
244
|
110
|
+3.0,—1.5
|
5.44
|
183
|
120
|
+3.0,—1.5
|
7.062
|
141
|
La velocidad de molienda de las bolas fundidas al moler el cemento
Material
|
Abrasion
|
Breakage
|
Size(mm)
|
Low Chrome Cast Ball
|
85-105g Cast Balls /Ton Cement
|
<2%
|
10-150mm
|
Medium Chrome Cast Ball
|
50-80g Cast Balls /Ton Cement
|
<1.5%
|
10-150mm
|
High Chrome Cast Ball
|
35-60g Cast Balls/Ton Cement
|
<1%
|
10-120mm
|
High Chrome Cylpebs
|
35-60g Cylpebs/Ton Cement
|
<1.5%
|
12×18-35×40
|
Low Chrome Cylpebs
|
65-95g Cylpebs/Ton Cement
|
<1%
|
12×18-35×40
|
Micro Cylpebs
|
6×6 8×8 10×10 12×12 15×15
|
Preguntas más frecuentes
1. ¿Puede proporcionar muestras gratis?
Respuesta: Sí, muestra gratis.
2. ¿Es usted un fabricante o una empresa comercial?
Respuesta: Somos un fabricante y tenemos una calificación de exportación independiente.
3. ¿Qué tipo de pago puede aceptar?
Respuesta: T / T, L / C, Paypal, Western Union
4. ¿Qué tal su control de calidad?
Responder: Para garantizar la calidad, tenemos un estricto sistema de control de calidad.
a) Realizaremos pruebas al comprar las materias primas.
b) Probaremos los productos cuando haya terminado.

PRODUCTOS POR GRUPO : Bola de molienda fundida > Bola de hierro de molienda de alto cromo